one of the most commonly used techniques to reduce the corrosion rate of rebar in concrete is addition substances named corrosion inhibitors into the concrete. corrosion inhibitor is chemical compounds that were added to concrete to prevent corrosion of steel in concrete. sodium nitrate is a type of anodic inhibitors that this study investigatesthe effect of this inhibitor on the properties of ...
This paper studies the corrosion behavior of B10 copper-nickel alloy in marine environment. Accelerated degradation test under marine environmental conditions was designed and performed based on the accelerated testing principle and the corrosion degradation mechanism. With the prolongation of marine corrosion time, the thickness of Cu₂O film increased gradually. Its corrosion product was Cu₂(O...
The corrosion behavior of pure Ti under a solid NaCl deposit in a wet O2 flow at 600 ̋C has been studied. The results showed that the corrosion rate was greatly accelerated by solid NaCl, which destroyed the compact and protective TiO2 scale to yield non-protective N4Ti5O12 and other products. Detailed scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDX), and...
The economies of coastal communities around the Great Lakes have historically been dependent upon maritime transportation. Urban ports and waterways continue to accommodate expanding trade, growth of tourism, and recreational boating. Even in this challenging economic period, planned expansions in the iron-ore, slab-steel, low-sulfur coal, and nonferrous metals industries and growing tourism in...
DURING COMBUSTION in the gas turbine, sulfur from the fuel reacts with sodium chloride from ingested air at elevated temperatures to form sodium sulfate. The sodium sulfate then deposits on the hot-section components, such as nozzle guide vanes and rotor blades, resulting in accelerated oxidation (or sulfidation) attack. This is commonly referred to as “hot corrosion.” Sulfur in the fuel is gen...
Eight retrieved metal-on-metal total hip replacements displayed corrosion damage along the cobalt-chromium alloy liner taper junction with the Ti alloy acetabular shell. Scanning electron microscopy indicated the primary mechanism of corrosion to be grain boundary and associated crevice corrosion, which was likely accelerated through mechanical micromotion and galvanic corrosion resulting from ...
This paper studied the effects of reinforcement corrosion on bond performance between rebar and concrete. Tests were carried out to evaluate the degradation of bond between reinforcing steel and concrete for different corrosion levels of reinforcing steel. A series of 20 specimens of different concrete strength with various reinforcing steel corrosion levels were designed and manufactured. Each...
The filling of strand corrosion products during concrete crack propagation is investigated experimentally in the present paper. The effects of stirrups on the filling of corrosion products and concrete cracking are clarified. A prediction model of crack width is developed incorporating the filling proportion of corrosion products and the twisting shape of the strand. Experimental data on cracki...
The withdrawal of effective but toxic corrosion inhibitors has provided an impetus for the discovery of new, benign organic compounds to fill that role. Concurrently, developments in the high-throughput synthesis of organic compounds, the establishment of large libraries of available chemicals, accelerated corrosion inhibition testing technologies, and the increased capability of machine learni...